It is made of high quality high-aluminum ceramic fiber cotton. After impurity and slag removal through kneading and stirring, and supplemented by various binders. Mainly used for repairing joints or damaged parts of launder, filter box, lining, distributor plate, thimble etc.
| Appearance | Grey white paste | ||
| Density | Paste | 1.6g/cm³ | |
| After 110℃*24h heating | 1.27g/cm³ | ||
| Line change rate | 800℃*1h | 0.40% | |
| Continuous service temperature | 950℃ | Refractoriness | 1260℃ |
| Thermal conductivity | 0.206kcal/mh | Bending strength | 4.5 MPa |
| Al2O3 | 35.40% | ||
Dip the mud knife in to water and take it out, brush it evenly to the gap or joint to be repaired, smooth the surface when finished. Dry it for 30 min to 1 hour if the thickness is 10mm, dry more than 3 hours if the thickness more than 30mm.
The degassing box is made of high-strength castable through integral casting and sintering, with good thermal shock resistance.
Tubular filtration equipment is installed between CFF filtration equipment and rolling mill.
The filter box lining is made of qualified castable and produced under sintering. It has high temperature resistance, corrosion resistance and good thermal insulation.
Caster tips have the advantages of uniform molten aluminium flow, laminar flow, no blockage, and the same temperature in the caster tip outlet.